Brown LH105 Resin Modeling Adhesives Epoxy Resin Materials CNC Machining process
Method of use
1. Respectively take agent 1 A and 1 B mix and stir to mix well.1 (weight ratio)
2. AB coating on the bonding agent mixture, and give us stick light pressure.
3. A glue adhesive items to shift of the banned or move in at least 10 minutes, otherwise it will seriously affect the bonding effect.
4. A glue adhesive items should be at least 4 hours before they can normal use, otherwise the curing effect and adhesive life would be affected.
5. Low temperature curing speed will slow down.
6. the appropriate surface treatment: then body surface of grease or oil to clear or grinding, remove foreign bodies to strengthen the bonding effect.
Matters needing attention
1. A, B two agent shall be stored in shady and cool place, two doses not piled up at the same time.
2. A, B two agent such as A large number of mix, causes rapid solidification of danger, should be especially careful, according to the usage.
3. After use, such as skin touch/consignment agent, the application of soap to clean.
4. Coated tools or containers are mixed, to shorten the service life.
Note: the product packaging in each group 2 kg, each box 10, will be A and B glue can be used according to the ratio of 1:1 and stir well,
Introduction
| Material | 108A | 108B | Mixed |
| Description | epoxy resin | curing agent | |
| mixing ration | 1 | 1 | |
| Color: | Beige | Yellow | Yellow |
| mixed time:500g,25°(min) | | | 30 |
| curing time before machining(20-25mm) (hours) | | | 60minutes |
| Hardness(Shore D): | | | 70-80 |
| Temperature Resistance(°C): | | | 100-150 |
| Compressive Strength(N/mm²): | | | 290-320(kg/cm2) |
| Flexural Strength(N/mm²): | | | 102(kg/cm2) |
Characteristics
easily shaped and machined,fine surface structure
Applications:
yacht model,benchmark model, system and sand-cast model, rapid prototype,etc.